1.FDA & ROHS certificate.
2.No limitation with product thickness .Can do deep curing .
3.High temperature resistance (can reach 0~250 degrees ) ,acid and alkali-resistance and aging resistance
4.Light viscosity and good flowability .easy for pouring operation .
5.Can be cured both at room temperature or be heated
6.Low shrinkage.Not releasing low molecular during cross-linking process .So the volume is constant .The shrinkage rate is less than 0.1%.
7.Favorable tensile and tear strength
8.High temperature resistance ,acid and alkali-resistance and aging resistance
9.High duplication times .aging -resistance
10.Tasteless.no flammable,safe and reliable
11.Customize as you need
| Item | Parameter | ||||
| G-810 | |||||
| Viscosity(cps) | 4000±500 | ||||
| Hardness(A°) | 10±2 | ||||
| Tensile Strength(kgf/cm²) | 30±2 | ||||
| Tear Strength(KN/M) | 12±1 | ||||
| Elongation(%) | 550±50 | ||||
| Shrinkage Rate(%) | 0.1% | ||||
| Mixing Ratio | 1:1 | ||||
| Life Time(Min) | 20~30 | ||||
| Curing Time (hr) | 2~3 | ||||
| Temperature(℃) | 25 | ||||
casting and injection shoe insole, healthy insole, prosthetic insole pad
Make soft products,as sex toys, sex dolls, body organs;
Body breast enhancers, bra pads, shoulder pads, paster, patches, antislip mat;
Human body shape, simulate robots, simulate props;
Simulate people,prostheses ,masks
Step 1: Prepare the molds
Prepare an perfect mold and clean it totally before operation .
＊Notes: Make sure your molds and operation tool cleaned up totally to avoid uncure problem .
Step 2: Mix part A and part B evenly
Take 100 G part A and 100 G part B and mix them evenly.
＊Notes: Addition cure mold making silicone rubber is two parts flowing liquid, Please follow the step strictly:
1. Weigh the two part exactly by electronic weight.
If any part not in exactly weight , it may cause changing of hardness , or even cause uncure problem.
2. Mix part A and part B evenly.
Otherwise the silicone rubber will be partly cured and this will give birth to difficulties in your final operation. What’s more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
Without exception, this step takes less than 10 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.
Step 4: Pouring casting
Clean your molds and brush a layer of release agent (detergent or soap water )on your molds .Pouring the vacuumed mixture silicone on your molds.
1. It is a kind of non-dangerous goods. This product should be sealed and placed in a cool and dry place which should keep from sunlight and rain .
2. Especially note that the silicone should not touch or mix with compounds including nitrogen, phosphorus, sulfur, tin, lead or metal organic acid.
3. Addition cure Silicone RTV-2 is an environmentally-friendly liquid silicone product is not easy to burn which can be stored and transported as non-hazardous goods.
4. The shelf life is 12months from the date of production.
It can be reused after reinspection when it exceeds the storage period.
It is a two-component platinum cure silicone rubber which can be cured at room temperature and also can be heat cured.The 10 shore a silicone rubber is high elastic and safe for shoe healthy insole injection casting