1.FDA & ROHS certificate.
2.No limitation with product thickness .Can do deep curing .
3.High temperature resistance (can reach 0~250 degrees ) ,acid and alkali-resistance and aging resistance
4.Light viscosity and good flowability .easy for pouring operation .
5.Can be cured both at room temperature or be heated
6.Low shrinkage.Not releasing low molecular during cross-linking process .So the volume is constant .The shrinkage rate is less than 0.1%.
7.Favorable tensile and tear strength
8.High temperature resistance ,acid and alkali-resistance and aging resistance
9.High duplication times .aging -resistance
10.Tasteless.no flammable,safe and reliable
| Item | Parameter | ||||
| RT-820 | |||||
| Viscosity(cps) | 5000±500 | ||||
| Hardness(A°) | 20±2 | ||||
| Tensile Strength(kgf/cm²) | 45±2 | ||||
| Tear Strength(KN/M) | 22±1 | ||||
| Elongation(%) | 500±50 | ||||
| Shrinkage Rate(%) | 0.1% | ||||
| Mixing Ratio | 1:1 | ||||
| Life Time(Min) | 20~30 | ||||
| Curing Time (hr) | 2~3 | ||||
| Temperature(℃) | 25 | ||||
It is a two-component platinum cure silicone rubber which can be cured at room temperature and also can be heat cured.It can be used for making soft silicone rubber material
1)Make soft products,as sex toys, sex dolls, body organs;
2) Body breast enhancers, bra pads, shoulder pads, paster, patches, antislip mat;
3) Human body shape, simulate robots, simulate props;
4)Simulate people,prostheses ,masks
1.Clear the model and tool totally before operation to prevent cure inhibition.
2.Take 100g of part A and 100g of part B and Mix them evenly in 2~3 minutes.
3.Get the mixed silicone into the vacuum pumping and de-air the bubble around 2~3 minuted .(if there is no vacuum machine ,please pour the mixture carefully and slowly down the inside of the mould frame so that less bubbles caused)
4.Clean your products and brush a layer of release agent (detergent or soap water )on your products
5.Pour the cacuumed mixed silicone into the model frame and cure it for 2-3 hours at normal temperaturet .It takes 30 minutes to cure when it is heated to 100 degree .
Notice:
As platinum cure silicone is platinum catalyst silicone which is very easy to cause cure inhibition , so please do remember thoroughly clean the model and tool before operation . Besides , please avoid the addition cure silicone contacting or mixing with the following material , otherwise the
silicone won’t be cured :
1.Liquid condensation silicone
2.tin compounds
3.Sulphur, sulfide and sulfur rubber materials.
4.Amine compounds as well as contains the amine materials.
5.Pewter solder flux.
1. It is a kind of non-dangerous goods. This product should be sealed and placed in a cool and dry place which should keep from sunlight and rain .
2. Especially note that the silicone should not touch or mix with compounds including nitrogen, phosphorus, sulfur, tin, lead or metal organic acid.
3. Addition cure Silicone RTV-2 is an environmentally-friendly liquid silicone product is not easy to burn which can be stored and transported as non-hazardous goods.
4. The shelf life is 12months from the date of production.
It can be reused after reinspection when it exceeds the storage period.
It is light viscosity and good flowability for easy pouring operation .It can be cured both at room temperature or be heated.
The favorable tensile and tear strength is good for penis ,bra and prosthetic parts casting
skin safe soft liquid silicone rubber for bra pad breast making 