tin cure mold making silicone rubber for candle soap molds
RTV-2 mould making silicone rubber is generally named as two-part silicone rubber that vulcanizes at room temperature. Part A is a flowable liquid, part B is the catalyst.
tin cure GC silicone rubber C-815 for soap candle molds
1.Good flowability and long working time
2.High tear and tensile strength
3.Easy de-mould from complex replica parts
4.Acid and alkali-resistance
5.Low linear shrinkage
6.Hundreds of replications times
7.Not oily
Technical Datasheet
| Item | Parameter | ||||
| C-815 | |||||
| Viscosity(cps) | 14000±500 | ||||
| Hardness(A°) | 15±2 | ||||
| Tensile Strength(kgf/cm²) | 25±2 | ||||
| Tear Strength(KN/M) | 16±1 | ||||
| Elongation(%) | 350±50 | ||||
| Shrinkage Rate(%) | 0.3% | ||||
| Mixing Ratio | 100:2 | ||||
| Life Time(Min) | 20~30 | ||||
| Curing Time (hr) | 2~3 | ||||
| Temperature(℃) | 25 | ||||
Product Application
Making molds for
- Cultural relic duplication, architectural decoration, statues
- Resin crafts,climbing holder
- Lighting ornaments, candles,hand soap
- Plaster, Gypsum, Cement, Concrete decorations
- Model design, product exploitation, etc.
- Artificial stone
How to Use
Step One: Prepare and clean the prototype. You must make sure your original moulds perfect.
Step Two: Mixing part A and part B evenly. Take 100g of part A and add 2g of part B and mix the silicone rubber and curing agent evenly.
Step Three: Vacuum pumping. Without exception, this step takes less than 10 minutes. Otherwise, it will cause a cross-linking reaction, and no further steps will be available.
Step Four: Pouring cast or brushing cast. After released the bubble, we can pour/brush the silicone rubber on the prototype
Pouring cast:
It is suitable for simple products with a smooth surface. Without any mould lines, which helps you save time and is easy for operation. Evenly and slowly pouring the mixed silicone rubber into the square frame. After the cross-linking reaction and the silicone rubber turns dry, you can take the products out. Thus, the mould has been done.
Brushing cast:
- Evenly brush the mixed silicone rubber on the product which is covered with mould spray with a brush or a brush pen.
- After the cross-linking reaction (about 30 minutes), brush a second coat which can increase the tension and tear strength of the mould.
- Cover a glass cloth on it after another 30 minutes of a second cross-linking reaction, and use a brush pen or a brush to avoid any interstices.
- Cover a third coat.
Product Storage
1. It is a kind of non-dangerous goods. This product should be sealed and placed in a cool and dry place which should keep from sunlight and rain .
2. The shelf life is 12months from the date of production.
It can be reused after reinspection when it exceeds the storage period.